dc.description.abstractEsta tesis tiene un enfoque cuantitativo, la cual propone evaluar la influencia de la permeabilidad en diseños de concreto con el uso de aditivos Sika WT – 100 y Sika WT – 200 en obras hidráulicas de Lima Metropolitana, debido a que estas estructuras almacenan y/o conducen grandes volúmenes de agua a una velocidad determinada, y éstas al tener contacto con el agua reducen su vida útil. Los objetivos de esta tesis son determinar la profundidad de penetración de agua bajo presión bajo la Norma Europea EN 12390 – 8 y la resistencia a la compresión bajo la Norma Técnica Peruana NTP 339.034; para finalmente, determinar la permeabilidad para diseños de concreto bajo la Norma Técnica Colombiana NTC 4483. Para lograr los objetivos mencionados, se diseñó y elaboró 144 probetas cilíndricas de concreto de 10 cm de diámetro y 20 cm de altura y 48 probetas cilíndricas de concreto de 15 cm de diámetro y de altura, de las cuales fueron 64 probetas de concreto patrón (sin uso de ningún aditivo), 64 probetas de concreto con aplicación de 2% de aditivo Sika WT – 100; y 64 probetas de concreto con aplicación de 1% de aditivo Sika WT – 200. Los resultados de los diseños de concreto patrón, WT – 100 y WT – 200 con una relación agua/cemento de 0.40, con respecto a la profundidad de penetración de agua bajo presión, fueron 40, 30 y 15 mm, respectivamente. Los resultados de los diseños de concreto patrón, WT – 100 y WT – 200, con respecto a la resistencia a la compresión a los 28 días con una relación agua/cemento de 0.40, fueron 637, 621 y 632 kg/cm2, respectivamente. Según la Norma Técnica Colombiana NTC 4483 y con los resultados obtenidos, se concluye que el diseño de concreto patrón y el diseño de concreto WT – 100 alcanzan una media permeabilidad y que el diseño de concreto WT – 200 alcanza una baja permeabilidad, con una relación agua/cemento de 0.40. This thesis has a quantitative focus, that propose to evaluate the influence of permeability concrete designs with the use of admixtures Sika WT – 100 and Sika WT – 200 in Metropolitan Lima waterworks, because these structures store and lead large volumes of water at a certain speed, and when these has contact with water reduces their useful life. The objectives of this thesis are to determine the depth of penetration of water under pressure under the European Norm EN 12390-8 and compressive strength under the Peruvian Technical Norm NTP 339.034; finally, determine the permeability of concrete designs under the Colombian Technical Norm NTC 4483. To achieve these objectives, we designed and developed 144 cylindrical concrete specimens 10 cm in diameter and 20 cm high and 48 cylindrical concrete specimens 15 cm in diameter and height, which were 64 concrete specimens pattern (without use of any admixture) concrete specimens 64 with application of 2% admixture Sika WT - 100; and 64 concrete specimens with application of 1% admixture Sika WT - 200. The results of pattern, WT – 100 and WT - 200 concrete designs with a water – cement ratio of 0.40, with respect to the depth of penetration of water under pressure, were 40, 30 and 15 mm, respectively. The results of pattern, WT – 100 and WT - 200 concrete designs with a water – cement ratio of 0.40, with respect to compressive strength at 28 days, were 637, 621 and 632 kg/cm2, respectively. According to the Colombian Technical Norm NTC 4483 and the obtained results, one can conclude that the pattern concrete design and WT - 100 concrete design reach a medium permeability and concrete design WT - 200 reaches a high permeability, with a water – cement ratio of 0.40.es_ES
dc.description.uriTesises_ES
dc.formatapplication/pdfes_ES
dc.language.isoeses_ES
dc.publisherUniversidad Ricardo Palmaes_ES
dc.rightsinfo:eu-repo/semantics/openAccesses_ES
dc.rights.urihttps://creativecommons.org/licenses/by-nc/3.0/es_ES
dc.sourceUniversidad Ricardo Palmaes_ES
dc.sourceRepositorio Institucional - URPes_ES
dc.subjectPermeabilidades_ES
dc.subjectDiseños de concretoes_ES
dc.subjectAditivoses_ES
dc.subjectProfundidad de penetración de agua bajo presiónes_ES
dc.subjectResistencia a la compresiónes_ES
dc.subjectRelación agua/cementoes_ES
dc.subjectPermeabilityes_ES
dc.subjectConcrete designes_ES
dc.subjectAdmixturees_ES
dc.subjectDepth of penetration of water under pressurees_ES
dc.subjectCompressive strengthes_ES
dc.subjectwater – cement ratioes_ES
dc.titleEvaluación de la permeabilidad en diseños de concreto con el uso de aditivos SIKA WT-100 y SIKA WT-200 en obras hidráulicas de Lima Metropolitanaes_ES
dc.typeinfo:eu-repo/semantics/bachelorThesises_ES
thesis.degree.disciplineIngeniería Civiles_ES
thesis.degree.grantorUniversidad Ricardo Palma. Facultad de Ingenieríaes_ES
thesis.degree.levelTítulo Profesionales_ES
thesis.degree.programPrograma de Titulación por Tesises_ES
thesis.degree.nameIngeniero Civiles_ES


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record

info:eu-repo/semantics/openAccess
Except where otherwise noted, this item's license is described as info:eu-repo/semantics/openAccess

Av. Benavides 5440 - Santiago de Surco Lima 33 Perú | Apartado postal 1801 | ( 0511 ) 708 0000

Sugerencias